1.0mm OK AristoRod 12.50 (18kg)

FREE Delivery on all orders over R2000 in GAUTENG

people viewed this product in the last 24 hours

R 945.00

ESAB

Welding Wire

Price is per 18kg spool.
OK Aristorod 12.50 is a bare Mn-Si-alloyed G3Si1/ER70S-6 solid wire for the GMAW of non-alloyed steels, as used in general construction, automotive components, pressure vessel fabrication and shipbuilding. OK Aristorod 12.50 is treated with ESAB’s unique Advanced Surface Characteristics (ASC) technology, taking MAG welding operations to new levels of performance and all-round efficiency, especially in robotic and mechanised welding. Characteristic features include excellent start properties; trouble-free feeding at high wire speeds and lengthy feed distances; a very stable arc at high welding currents; extremely low levels of spatter; low fume emission; reduced contact tip wear and improved protection against corrosion of the wire.
Typical Tensile Properties
AWS CO2 (C1)
Condition
Elongation
Tensile Strength
Yield Strength
Testing Temperature
Testing Time
As Welded
30 %
530 MPa
430 MPa
-
-
EN 80Ar/20CO2 (M21)
Condition
Elongation
Tensile Strength
Yield Strength
Testing Temperature
Testing Time
As Welded
26 %
560 MPa
470 MPa
-
-
Stress Relieved
28 %
495 MPa
370 MPa
620 °C
15 hr
EN CO2 (C1)
Condition
Elongation
Tensile Strength
Yield Strength
Testing Temperature
Testing Time
As Welded
25 %
540 MPa
440 MPa
-
-
Charpy V-Notch Properties
AWS CO2 (C1)
Condition
Impact Value
Testing Temperature
Stress Relieved Testing Temp
Stress Relieved Testing Time
As Welded
75 J
-30 °C
-
-
EN 80Ar/20CO2 (M21)
Condition
Impact Value
Testing Temperature
Stress Relieved Testing Temp
Stress Relieved Testing Time
As Welded
130 J
20 °C
-
-
As Welded
120 J
-20 °C
-
-
As Welded
100 J
-30 °C
-
-
As Welded
90 J
-40 °C
-
-
As Welded
70 J
-50 °C
-
-
Stress Relieved
120 J
20 °C
620 °C
15 hr
Stress Relieved
90 J
-20 °C
620 °C
15 hr
EN CO2 (C1)
Condition
Impact Value
Testing Temperature
Stress Relieved Testing Temp
Stress Relieved Testing Time
As Welded
110 J
20 °C
-
-
As Welded
75 J
-30 °C
-
-
Weld Metal Analysis
CO2 (C1)
Mn
C
Si
Ti+Zr
-
-
-
<0,01 %
80Ar/20CO2 (M21)
Mn
C
Si
Ti+Zr
-
-
-
<0,01 %
wire composition
Mn
C
Si
Ti+Zr
1.46 %
0.08 %
0.85 %
-
Approvals:
ABS; 3Y SA; BV; SA3YM; CE; EN 13479; DB; 42.039.29; DNV-GL; III YMS; LR; 3YS H15; PRS; 3YS; RS; 3Y40MS; VdTÜV; 10052; CWB; B-G 49A 3 C1 S6 (B-G 49A 3 C G6); PV,ZG; JIS; YGW12 (C1); ZG; NAKS/HAKC; 1.0-1.6 mm; PV; NAKS/HAKC; 1.2-1.6 mm; ZG; RINA; 3Y S; ZG; RINA; 3Y S; PV
Classifications:
EN ISO 14341-A; G 38 3 C1 3Si1; Weld Metal; EN ISO 14341-A; G 42 4 M20 3Si1; Weld Metal; EN ISO 14341-A; G 42 4 M21 3Si1; Weld Metal; EN ISO 14341-A; G 3Si1; Wire Electrode; SFA/AWS A5.18; ER70S-6; Wire Electrode; CSA W48; B-G 49A 3 C1 S6; Wire Electrode; JIS Z 3312; YGW 12 (C1); Wire Electrode
Alloy Type:
Carbon-manganese steel (Mn/Si-alloyed)